本研究生物力學檢測用假骨為美國Sawbone公司Open Cell R

本研究生物力學檢測用假骨為美國Sawbone公司Open Cell Rigid Foam系列，其材料為聚氨酯(Polyurethane)，大小為13cm ×18cm × 4cm，且其密度為0.12 g/cc，抗壓強度為0.28 MPa，，如圖5為人造假骨實際圖示。

Kết quả (Anh) 1:

This research used in biomechanical testing bone for United States Sawbone Open Cell Rigid Foam series, the material is polyurethane (Polyurethane), size of 13cmx18cmx4cm and the density of 0.12 g/cc, 0.28 MPa compressive strength, and bone actual icon in Figure 5 is false.

Kết quả (Anh) 2:

In this study, the false detection of bone biomechanical U.S. Sawbone Company Open Cell Rigid Foam series, which material is a polyurethane (Polyurethane), the size of 13cm × 18cm × 4cm, and having a density of 0.12 g / cc, a compressive strength of 0.28 MPa, Figure 5 illustrates the actual human bone fraud.

Kết quả (Anh) 3:

The study on biomechanical testing with artificial bone for American sawbone company open cell rigid foam series. The material for polyurethane (polyurethane), size 13cm x 18 cm x 4 cm and the density for 0.12 g/cc, compressive strength is 0.28 MPa and, as shown in Figure 5 is the actual schema of the artificial bone.